Grunlan's fire-resistant coating research featured in Textile World magazine

Photo of Dr. Jaime GrunlanDr. Jaime Grunlan's research into fire-resistant materials is featured in the November/December 2012 issue of Textile World magazine, a leading publication in the textiles industry.

The article highlights Grunlan's development of a thin polymer coating that keeps fabric and polyurethane-foam-based furniture from going up in flames.

Grunlan, an associate professor in the Department of Mechanical Engineering and holder of the Gulf Oil/Thomas A. Dietz Career Development Professorship, works with polymer nanocomposites that have properties similar to those of metals and ceramics — conducting electricity, for instance — while maintaining properties of polymers, such as low density.

“We can now make cotton fabric that doesn’t burn at all,” Grunlan said. (Pictured right: Cotton fabric after a vertical flame test, where a flame touches the fabric for 12 seconds.)Photo of cotton fabric

Grunlan's technology involves covering every microscopic fiber in a fabric with a thin composite coating of two polymers that exhibit an intumescent effect, producing a protective carbon foam coating when exposed to high temperatures.

The thin films are about one-tenth of a micron thick, or about one-thousandth the thickness of a human hair, and are created with the layer-by-layer assembly technique in which the coating is deposited onto the surface of the fiber being coated. This layer-by-layer process allows Grunlan to control the thickness of the coating down to the nanometer level.

Grunlan says the technology will be suitable for clothing, including children's clothing; lab coats; and medical clothing for both doctors and patients. It can even be used in military camps, where a fire in a single tent can wipe out an entire camp.

Photo of treated foamBut the technology's applications go far beyond just clothing and fabric. The coating could be used in foams, such as those found in sofas, mattresses, theater and auditorium seats, airplane seat cushions, and building insulation. (Pictured left: Foam cut through the middle after being exposed to fire from a butane torch.) 

On polyurethane foam, a coating of chitosan (a natural material extracted from shrimp and lobster shells) and clay is deposited to eliminate melt dripping during burning. The nanocomposite mixture coats the interior walls of foam. The result is that when burned, the treated foam keeps its shape instead of puddling at high temperatures like untreated polyurethane foam does. This quality eliminates the “melt-dripping” effect that further spreads fires.

"It's like we're building a nano-brick wall within each cell of the foam," Grunlan says.

That brick wall keeps the foam from being destroyed. And the coating is so thin that it adds only 4 to 5 weight-percent to the foam and does not negatively alter its color, texture or flexibility.

Grunlan holds a joint appointment in the Artie McFerrin Department of Chemical Engineering and in the interdisciplinary Materials Science and Engineering Program.